Specialty Emulsions


Type

Product Name

Typical Physical Properties

Characteristic

Appearance

Solid,%

pH

MFFT,

Hydroxyl Acrylic Emulsions

Coxcen™ 8300

Milky white liquid

41±1

7±1

30

The polymer film has high hardnees, high gloss, and good anit-corrosion property. The emulsion has relatively high reactivity, and can be used for curing with PU curing agent at room temperature, and also with ammonium-based resin at high temperature. The hardness of the film can reach 2H - 3H. Suitable for water-borne, high-gloss, scrub-resistance top coats for metal surfaces. Used in baked paints from low to high temperatures. Hydroxyl content: 3.3%.

Coxcen™ 8338

Milky white translucent liquid

46±1

7±1

30

Hydroxyl acrylic emulsion for water-borne industrial coatings with film properties in high hardness, high gloss, richness, and corrosion-resistance. Relatively high recativity, and can be used with PU curing agents to cure at room or low temperatures, or used with amine resins to cure at high temperatures.Suitable for water-borne metal coatings with requiremtns in high gloss and scratch-resistance. Also used for base coat. Good general applicability. Hydroxyl content: 3.3%.

Coxcen™ 8308

Milky white translucent liquid

47±1

7±1

32

One-pack emulsion for baking paint, with film properties in high hardness, high gloss, and richness.Curing temperature can be as low as 100 - 120℃ to achive good curing results. Fast drying rate and hardness buiildup. No VOC.Can be used in both base coat and top coat for metals. No need for additional catalysts. Strong general applicability.

Coxcen™ 8350

Milky white liquid

49±1

7±1

42

Hydroxyl acrylic emulsion for water-borne high-gloss industrial coatings with film properties in high hardness, high gloss, and scratch-resistance. Can be used with PU curing agents to cure at room and low temperatures.Also used with amine resins to cure at high temperatures.The hardness can reach up to 3H. Suitable for water-borne metal coatings with requirements in high-gloss and scratch resistance. Hydroxyl content: 4.1%.

Coxcen™ 8360

Milky white liquid

45±1

7±1

18

Hydroxyl acrylic emulsion with some degree of elasticity. Balanced hardness and elasticity. Can be used with PU curing agents to cure at room and low temperatures, and with amine resins to cure at high temperatures. Suitable for water-borne metal coatings with requirements in solvent resistance and high elasticity. Good general applicability. Hydroxyl content: 2.9%。

Coxcen™ 8380

Milky white liquid

45±1

7±1

32

Hydroxyl acrylic emulsion for water-borne industrial coatings with high weatherability. Good film properties in high hardness, high gloss, and scratch resistance. Suitable for outdoor top coat applications. Can bes used with PU curing agents to cure at room and low temperatures, and with amine resins to cure at high temperatures. Hydroxyl content: 3.2%.

Coxcen™ 8390

Transparent liquid

65±1

3±1

Water soluble hydroxyl acrylic resin with excellent water solubility and even better compatibiity with amine resins. Dense film formation and fast hardness buildup. Suitable for base coat. Also suitable for top coat with amine based baking paint. Hydroxyl content: 3.8%.

Acrylic Emulsions

Coxcen™ 8190

Milky white liquid

46±1

8±1

30

One-pack emulsion for water-borne ready-mixed metal paints with excellent early water-resistance. Good adhesion. Salt spray resistance can reach 96 hours. Can be used for two-in-one formulations.

Coxcen™ 8191

Milky white liquid

47±1

8±1

29

General-purpose acrylic emulsion specially developed for water-borne metal coatings. One-pack film-forming emulsion with balance properties in film formation, hardness, and corrosion resistance. Good adhesion to metal substrates. Salt spray resistance is greater than 120 hours. Suitable for water-borne metal base coat and two-in-one formulations.

Coxcen™ 8192

Milky white liquid

47±1

8±1

35

One-pack emulsion for high-gloss top coat with film properties in high gloss, good water resistance, and weatherability. Suitable for the top coat of metal coatings.

Coxcen™ 8765

Milky white liquid

42±1

8±1

34

Acrylic emulsion specially developed for water-borne metal coatings. The polymer film has good hardness, water resistance, water-whitening resistance, corrosion resistance. Salt spray resistance is greater than 240 hours. Good adhesion to metal substrates and good weatherability. Suitable for water-borne metal base coat, as well as two-in-one formulations.

Coxcen™ 8259

Milky white liquid

46.5±1

8±1

58

A high-gloss and high-hardness acrylic emulsion specially developed for water-borne metal top coatings. The emulsion is an one-pack film forming polymer with relativly high gloss. The hardness of the film can reach 1H and above. At the same time, the film has good water resistance and alkali resistance. Suitable for water-borne metal top coats.

Coxcen™ 8799

Milky white liquid

46±1

8.5±1

32

Acrylic emulsion especially designed for water-borne metal coatings on rusty substrates.The emulsion polymer contains functional groups reactive with rusty substrates, preventing the outgrowth of the rust. Very good adhesion with metal substrates and corrsoion resistance property. Does not contain components such as tannic acid which may cause the change in film properties. Can be used in various pigmented formulations. When used in metal base coat, flash rust can be inhibited with the use of any flash rust inhibitors, while better results can be achieved with the use of flash rust inhibitors. Suitable for metal base coat on rusty substrates, Also used in two-in-one formulations.

Epoxy Acrylic

Coxcen™ 8066

Milky white liquid

46±1

7.5±1

20

Aqueous epoxy acrylic resin. No organic solvent. Very good ahdesion to different metal substrtates.Good water resistance. Suitable for metal base coat.

Dry Self-crosslinking Emulsion

Coxcen™ 8089

Milky white liquid

47±1

7.5±1

22

Acrylic emulsion with dry self-crosslinking characteristic. Fast drying speed. Will gradually croslinking in ambient air, thus greatly enhancning the overall propertis of the polymer film while not risking film yellowness. Suitable for water-borne coatings with high requirement on corrosion resistance.

Aqueous UV

Coxcen™ 8059

Milky white liquid

48±1

7.5±1

UV curable acrylic emulsion. No organic solvents with low odor. Good flexibility with different formulations.Can be adjusted acfroding to different working viscosities. Self-drying. Excellent paint films can be obtaind with UV curing after drying. Very high film hardness and high gloss, and very good solvent resistance.

Emulsion for Low-T Baking

Coxcen™ 8500

Milky white translucent liquid

42±1

7.5±1

33

Acrylic emulsion for low temperature baking paints. Cure with curing agent C-285 at 80 - 120℃ to obtain films of high gloss and high hadrness. Very good water resistance, solvent resistance, and corrosion resistance.

Curing Agent for Low-T Baking

Coadd™ C-285

Milky white liquid

64±1

7±1

Curing agent for low temperature baking paints. Used with Coxcen™8500 emulsion at temperature of 80 - 120℃.

Emulsions for Aqueous Inks

Coxcen™ 9127

Milky white translucent liquid

41±1

7.5±1

7

Suitable for aqueous base coat in printing applications. Very low VOC. Excellent adhesion to different substrates such as platics, aluminum foils, and paper boards. Excellent weatherbility, water resistance, and solvent resistance. Excellent ink re-dissolving ability. Long-lasting adhesion with follow-up inks and varnishes.

Coxcen™ 9706

Milky white translucent liquid

41±1

8±1

8

A polymer resin for water-borne ink formulations. Very low VOC. Excellent pigment dispersion and grinding property. Excellent ink re-dissoling ability. Excellent adhesion to various substrates such as aluminum foils, and thin films.

Coxcen™ 9800

Milky white translucent liquid

46±1

7.5±1

52

Hard-film forming emulsion for aqueous ink formulations. Providing hardness and resistance properties. Combined with soft polymers in the formulations as binders for the aqueous inks. Good water resistance and alcohol resistance.

Coxcen™ 9900

Milky white translucent liquid

45±1

7.5±1

< 0

Film-forming emulsion for aqueous ink formulations with low film-forming temperature and good water resistance and alcohol resistance.